Yixing Shenzhou HDPE Geomembrane Ground cover
| No. | Properties | Test Method | Test Value | |||||||
| 1 | Thickness(mm) | ASTM D5199 | 0.50 | 0.75 | 1.00 | 1.25 | 1.50 | 2.00 | 2.50 | 3.00 |
| 2 | Density (g/cm2) | ASTM D1505 | 0.939 | |||||||
| 3 | Tensile Propeties | |||||||||
| Yield Strength(N/mm) | ASTM D6693 | 7 | 11 | 15 | 18 | 22 | 29 | 37 | 44 | |
| Break Strength(N/mm) | 13 | 20 | 27 | 33 | 40 | 53 | 67 | 80 | ||
| Yield Elongation % | Type IV | 12 | ||||||||
| Break Elongation % | 700 | |||||||||
| 4 | Tear Resistance/N | ASTM D1004 | 62 | 93 | 125 | 156 | 187 | 249 | 311 | 374 |
| 5 | Puncture Resistance/N | ASTM D4833 | 160 | 240 | 320 | 400 | 480 | 640 | 800 | 960 |
| 6 | Stress Crack resistance/hr |
ASTM D5397 |
300 | |||||||
| 7 | Carbon Black | |||||||||
| Carbon Black Content % | ASTM D1603 | 2.0-3.0 | ||||||||
| Carbon Black Dispersion | ASTM D5596 |
Carbon black dispersion(only near spherical agglomerates)for 10 different views 9 |
||||||||
| 8 | Oxidative Induction Time(OIT) | |||||||||
| Standard OIT/min | ASTM D3895 | 100 | ||||||||
| High Pressure OIT/min | ASTM D5885 | 400 | ||||||||
| 9 | Oven Aging at 85°C | |||||||||
| Standard OIT-% retained after 90 days | ASTM D3895 | 55 | ||||||||
| High pressure OIT-% retained after 90 days | ASTM D5885 | 80 | ||||||||
| 10 | UV Resistance | |||||||||
| Standard OIT retained after 1600 hrs | ASTM D3895 | 50 | ||||||||
| High pressure OIT retained after 1600 hrs | ASTM D5885 | 50 | ||||||||
| 11 | Low tempreture impact brittle property at -70°C | _ | Pass | |||||||
| 12 | Permeability g·cm/(cm2)·Pa | _ | ≤1.0×10-13 | |||||||
| 13 | Dimensional Stability/% | _ | ±2 | |||||||
Feature of HDPE GEOMEMBRANE